Welcome to the DrVAX Community.
If this is your first visit, be sure to
check out the FAQ by clicking the
link above. You may have to register
before you can post: click the register link above to proceed. To start viewing messages,
select the forum that you want to visit from the selection below.
As our community grows, it has become a bit harder to keep up with new posts. Here are some things that will help.
When you view a topic, there are two tabs at the top of the posts, one is called "posts," the other is called "latest activity." If you click on "posts," the newest replies will be on the bottom. If you click on "latest activity," the latest responses will be on the top.
If you want to be notified when new topics are created in a forum make sure you click on the subscribe button on the top right of the page.
Thanks for participating in the DrVax community. Irv
Folks,
Forum user Geit gave me a helpful push and I learned how to added additional attachment types to our forums. You can now attach/upload FCStd, F3d and STL files. In addition I have increased the PDF file size limit so I can more easily upload DrVAX video slides decks.
All the best. Irv
I still deal with stringing issues from time to time but it seems more to do with your retraction speed and distance. Dr. Vax has some videos on this so do a search on YouTube for them.
I got a spool of the hatchbox wood pla. Did a small print. I get a bit of stringing.
What causes stringing. I had to run it at 215 to get it working
Usually stringing gets caused by to low temperature. The filament is less fluid and on retract the string does not rip appart. It is kind of like when you touch a hot glue ball. You instantly get fat stringing, as the temperature on the outside is not hot enough, not fluid enough.
215°C is actually not uncommon. The print temperature on the box/spool is a guideline for speed. So the lower temperature is for slow print speed and the higher value is for higher print speed. I usually print on the upper end of the scale at 215°C with 55mm/s for plain PLA to be on the save side.
In addition to that, when dealing with "mixed" filament you need to take account that the temperature gets shiftet, as the wood particles are not melting and do not properly transfer the heat, while some metal flake glitter may be. So when normal 100% color prints fine at 210°C the wood one may not, unless it is just a (wood) color which usually has a next to no effect on the required print temperature.
So you need to compensate for particles in the filament and I guess the temperature on the box/spool just represents the pure plastic.
I'm with Geit. I mean, how abrasive is sawdust? More than bare filament? Sure. As abrasive, or more abrasive, than glass or carbon fiber, or metallic filament? I doubt it.
BTW Geit, what does "crap the head the stuff up" mean?
Hatchbox is not at all abrasive and on my third roll now it has never clogged a nozzle on me. I have had clogged nozzles before but only on bowden fed extruders.